Title: | A utilização da difração de neutrões na determinação do perfil de tensões residuais em revestimentos por soldadura | Other Titles: | The use of neutron diffraction for the determination of the in-depth residual stresses profile in weld coatings | Authors: | Marques, Maria José Batista, A. C. Nobre, J. P. Loureiro, Altino Kornmeier, Joana R. |
Keywords: | Difração de neutrões; Tensões residuais; Revestimentos; Arco submerso; Neutron diffraction; Residual stresses; Cladding; Submerged arc welding | Issue Date: | 2013 | Publisher: | Associacao Brasileira da Soldagem | Project: | PTDC/EME-TME/103845/2008 PestC/FIS/UI0036/2011 Comissão Europeia o financiamento da missão através do 6º Programa Quadro, “Strengthening the European Research Area, Research Infrastructures”, Contract RII3-CT-2003-505925. |
Serial title, monograph or event: | Soldagem e Inspecao | Volume: | 18 | Issue: | 2 | Abstract: | A técnica de difração de neutrões é usada neste artigo para estudar amostras ferríticas, revestidas com aços inoxidáveis austeníticos
através de soldadura por arco submerso. Este procedimento é frequentemente usado no fabrico de equipamentos de processo para as
indústrias química e nuclear, por facilidade de execução e razões económicas. A principal desvantagem deste processo de revestimento
é a fissuração que frequentemente ocorre na interface material base/soldadura, potenciada pela presença de tensões residuais resultantes
da operação de soldadura, a qual pode ser minimizada com a realização de tratamentos térmicos de relaxação de tensões.
As amostras foram produzidas a partir de placas em aço ao carbono, tendo uma das superfícies sido revestida com dois tipos de aço
inoxidável. Para a primeira camada foi usado um elétrodo EN 12072 – S 23 12 2 L e para a segunda e a terceira camadas foi usado um
elétrodo EN 12072 – S 19 12 3 L. Após a soldadura, as amostras foram submetidas a um tratamento térmico de relaxação de tensões,
durante 1 hora, à temperatura de 620°C. Os perfis de tensões residuais obtidos por difração de neutrões evidenciam a relaxação de
tensões residuais após o tratamento térmico realizado. A técnica de difração de neutrões revelou-se muito adequada na avaliação de
tensões residuais neste tipo de ligações. The neutron diffraction is a non-destructive technique, particularly suitable for the analysis of residual stress fields in welds. The technique is used in this article to study ferritic samples, coated by submerged arc welding using stainless steel filler metals. This procedure is often used for manufacturing process equipment for chemical and nuclear industries, for ease of implementation and economic reasons. The main disadvantage of that processes is the cracking phenomenon that often occurs at the interface between the base material and coatings, which can be minimized by performing post-weld stress relief heat treatments. The samples analyzed in this study were made of carbon steel plates, coated by submerged arc welding two types of stainless steel filler metals. For the first layer was used one EN 12 072 - S 2 U 23 12 electrode, while for the second and third layers were used an EN 12 072 - 19 12 3 S L electrode. After cladding, the samples were submitted to a post-weld heat treatment for 1 hour at 620°C. The residual stress profiles obtained by neutron diffraction evidence the relaxation of residual stress given by the heat treatment. |
URI: | https://hdl.handle.net/10316/109811 | ISSN: | 0104-9224 | DOI: | 10.1590/S0104-92242013000200008 | Rights: | openAccess |
Appears in Collections: | FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
The-use-of-neutron-diffraction-for-the-determination-of-the-indepth-residual-stresses-profile-in-weld-coatingsSoldagem-e-Inspecao.pdf | 2.32 MB | Adobe PDF | View/Open |
Page view(s)
127
checked on Oct 2, 2024
Download(s)
45
checked on Oct 2, 2024
Google ScholarTM
Check
Altmetric
Altmetric
This item is licensed under a Creative Commons License