Title: | Influence of Ag content on mechanical and tribological behavior of DLC coatings | Authors: | Manninen, N. K. Ribeiro, F. Escudeiro, A. Polcar, T. Carvalho, S. Cavaleiro, A. |
Keywords: | Ag–DLC; Structure; Mechanical properties; Tribology; Wear mechanisms | Issue Date: | 15-Oct-2013 | Publisher: | Elsevier | Citation: | MANNINEN, N. K. [et. al] - Influence of Ag content on mechanical and tribological behavior of DLC coatings. "Surface and Coatings Technology". ISSN 0257-8972. Vol. 232 (2013) p. 440-446 | Serial title, monograph or event: | Surface and Coatings Technology | Volume: | 232 | Abstract: | Ag–DLC coatings with Ag contents ranging from 1.3 at.% to 13.1 at.% were deposited by DC magnetron sputtering. The coatings were characterized with respect to their structure (by means of XRD and Raman spectroscopy), mechanical and tribological properties (by scratch test, nanoindentation, residual stress measurements and pin-on-disk test). The incorporation of 13.1 at.% Ag resulted in the formation of Ag grains of 2–3 nm which promoted the increase of graphite like bonds organized in rings. Regarding the mechanical properties, no variations were found for films with Ag contents lower than 13 at.%; a reduction of both hardness and compressive residual stress was then observed for higher values. Pin-on-disk tests were performed at two different contact pressures (690 MPa and 1180 MPa) in dry sliding conditions against a zirconia counterpart. For the lower contact pressure the variations in the wear rate are well correlated with the coating structure and mechanical properties, while for the higher contact pressure the presence of Ag is relevant and Ag–DLC coatings are showing higher wear rate than DLC one. SEM analysis revealed the formation of Ag aggregates on the wear track and adhesion of silver to the counterpart. | URI: | https://hdl.handle.net/10316/27397 | ISSN: | 0257-8972 | DOI: | 10.1016/j.surfcoat.2013.05.048 | Rights: | openAccess |
Appears in Collections: | I&D CEMMPRE - Artigos em Revistas Internacionais FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Influence of Ag Content on Mechanical and Tribological behavior of DLC Coatings.pdf | 3.62 MB | Adobe PDF | View/Open |
SCOPUSTM
Citations
103
checked on Aug 26, 2024
WEB OF SCIENCETM
Citations
1
97
checked on Sep 2, 2024
Page view(s)
331
checked on Sep 3, 2024
Download(s) 50
437
checked on Sep 3, 2024
Google ScholarTM
Check
Altmetric
Altmetric
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.