Title: | Mechanical and wear behaviours of nano and microfilled polymeric composite: effect of filler fraction and size | Authors: | Antunes, P. V. Ramalho, A. Carrilho, E. V. P. |
Keywords: | Filler content and dimension; Polymeric composites; Wear resistance | Issue Date: | Sep-2014 | Publisher: | Elsevier | Citation: | ANTUNES, P. V.; RAMALHO, A.; CARRILHO, E. V. P. - Mechanical and wear behaviours of nano and microfilled polymeric composite: effect of filler fraction and size. "Materials & Design". ISSN 0261-3069. Vol. 61 (2014) p. 50–60 | Serial title, monograph or event: | Materials & Design | Volume: | 61 | Abstract: | The addition of ceramic reinforced material, SiC particles, to resin matrices, results in the improvement of the overall performance of the composite, allowing the application of these materials as tribo-materials in industries such as: automotive, aeronautical and medical. Particle-reinforced polymeric composites are widely used as biomaterials, for example as dental filler materials and bone cements. These reinforced composites have improved mechanical and tribological performance and have higher values of elastic modulus and hardness, and also reduce the shrinkage during the polymerisation compared with resin matrices. However, the effect of the filler level in mechanical and tribological behaviour is not quite understood. The aim of this work is to determine the influence of the particle volume fraction and particle size in the wear loss of the composites and their antagonists. Reciprocating wear tests were conducted using a glass sphere against resin polyester silica reinforced composite in a controlled medium, with an abrasive slurry or distilled water. For 6 μm average particle dimension, seven particles contents were studied ranging from 0% to 46% of filler volume fraction (FVF). Afterwards, filler volume fractions of 10% and 30% were selected; and, for these percentages, 7 and 4 average particle dimensions were tested and were evaluated regarding their wear behaviour, respectively. The reinforcement particle dimensions used ranged from 0.1 μm to 22 μm with the 10% filler fraction, and for 30% of filler content the range extended from 3 μm to 22 μm. The results allow us to conclude that in an abrasive slurry medium the composite abrasion resistance decreases with the increase of the particle volume fraction, in spite of the accompanying rise in hardness and elastic modulus. With constant FVF, and abrasive slurry, the composite wear resistance increases with increasing average particle dimension. In a distilled water medium and with several FVF values, the minimum wear was registered for a median particle content of 24%. In this medium and with constant FVF the highest wear resistance occurred for average reinforcement particles of 6 μm. The removal mechanisms involved in the wear process are discussed, taking into account the systematic SEM observations to evaluate the wear mechanisms. | URI: | https://hdl.handle.net/10316/27925 | ISSN: | 0261-3069 | DOI: | 10.1016/j.matdes.2014.04.056 | Rights: | openAccess |
Appears in Collections: | I&D CEMMPRE - Artigos em Revistas Internacionais |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Mechanical and wear behaviours of nano and microfilled polymeric composite.pdf | 3.02 MB | Adobe PDF | View/Open |
SCOPUSTM
Citations
65
checked on Sep 30, 2024
WEB OF SCIENCETM
Citations
5
57
checked on Sep 2, 2024
Page view(s) 10
993
checked on Sep 24, 2024
Download(s) 50
685
checked on Sep 24, 2024
Google ScholarTM
Check
Altmetric
Altmetric
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.