Título: | Properties of Electrospun TiO2Nanofibers | Autor: | Caratão, Bianca Carneiro, Edgar Sá, Pedro Almeida, Bernardo Carvalho, Sandra |
Data: | 2014 | Projeto: | PEST-C/FIS/UI607/2011 project Matepro—Optimizing Materials and Processes, ref. NORTE-07-0124-FEDER-000037 “Programa Operacional Regional do Norte” (ON.2—O Novo Norte), under the “Quadro de Referência Estratégico Nacional” (QREN), through the “Fundo Europeu de Desenvolvimento 8 Regional” (FEDER) |
Título da revista, periódico, livro ou evento: | Journal of Nanotechnology | Volume: | 2014 | Resumo: | Titaniumoxide filled polyvinylpyrrolidone (PVP) composite nanofibers have been prepared via a simple electrospinning technique. The combination of good TiO2 properties with its high surface area leads these nanofibers into having a vast applicability such as cosmetics, scaffolds for tissue engineering, catalytic devices, sensors, solar cells, and optoelectronic devices. The structural and chemical properties of the prepared samples have been studied. The presence of the TiO2 phase on the nanofibers was confirmed. An anatase to rutile transformation was observed at 600∘C. Regarding the thermogravimetric and differential thermal analysis (TGA/DTA), the TIP decomposition and the PVP evaporation at 225∘C were verified. | URI: | https://hdl.handle.net/10316/102607 | ISSN: | 1687-9503 1687-9511 |
DOI: | 10.1155/2014/472132 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Properties-of-electrospun-TiOsub2sub-nanofibersJournal-of-Nanotechnology.pdf | 4.27 MB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
41
Visto em 23/set/2024
Citações WEB OF SCIENCETM
33
Visto em 2/set/2024
Visualizações de página
63
Visto em 24/set/2024
Downloads
36
Visto em 24/set/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Este registo está protegido por Licença Creative Commons