Title: | Comportamento mecânico de juntas T soldadas por fricção linear na liga AA6082 | Other Titles: | Mechanical behavior of friction stir welded (FSW) T-joints in the AA6082 alloy | Authors: | Carvalho, Diogo Albano Cavaleiro Ventura de | Orientador: | Costa, José Domingos Moreira da Loureiro, Altino de Jesus Roque |
Keywords: | Friction Stir Welding; Junta T; T-Lap; T-Butt; Defeitos; Friction Stir Welding; T joint; T-Lap; T-Butt; Defects | Issue Date: | 27-Jul-2015 | Place of publication or event: | Coimbra | Abstract: | A soldadura por fricção linear (FSW), surge atualmente como um processo de ligação, de grande interesse na produção de juntas T. Estas soldaduras apresentam, frequentemente, defeitos como cavidades e linhas de óxidos, além da redução da espessura na pele da junta T.
Neste trabalho estudou-se a solução para o problema de redução de espessura, a otimização da geometria de ferramenta e de parâmetros de soldadura para a obtenção de soldaduras sem defeitos e a possível melhoria do comportamento mecânico de juntas T na liga de alumínio 6082-T6. Para o efeito foram realizadas análises morfológicas, ensaios de dureza, tração e fadiga seguida de análise fratográfica, para soldaduras nos dois tipos de configuração de junta, T-Butt e T-Lap.
Concluiu-se que, com a ferramenta progressiva usada na configuração T-Butt é possível eliminar a linha de óxidos e que a configuração T-Lap elimina totalmente a redução de espessura da pele. Nowadays, friction stir welding (FSW) appears as a joining process of increasing interest in the production of T joints. This type of welds frequently present defects such as cavities or oxides lines, besides the thickness reduction in the skin of the T joint. This paper work will try to present a possible solution to the thickness reduction problem, an optimization of welding parameters to obtain defect free welds and a possible improvement in mechanical behavior of this type of joint in the 6082-T6 aluminum alloy. In order to do that, several analysis and tests will be conducted, ranging from morphologic analysis to hardness, stress and fatigue tests followed by fracture analysis, in two types of joint configurations, T-Butt and T-Lap. It was concluded that the removal of the oxide lines are possible using the progressive tool design and also that the joint configuration, T-Lap, was able to completely eliminate the thickness reduction problem. |
Description: | Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra. | URI: | https://hdl.handle.net/10316/38975 | Rights: | openAccess |
Appears in Collections: | UC - Dissertações de Mestrado FCTUC Eng.Mecânica - Teses de Mestrado |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Comportamento mecanico de juntas T soldadas por friccao linear na liga AA6082.pdf | 6.36 MB | Adobe PDF | View/Open |
Page view(s) 50
520
checked on Aug 14, 2024
Download(s) 50
672
checked on Aug 14, 2024
Google ScholarTM
Check
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.